Mechanism and kinetic of piezo-catalytic desulfurization of model and actual fuel samples over CeO/SrO nanocomposite at room temperature.

SO emissions are primarily caused by compounds containing sulfur in petroleum and fuels, which lead to severe air pollution. For this reason, it is necessary to develop a fast and simple desulfurization method in order to comply with ever-increasing environmental regulations. The newly discovered piezo-catalyst nanocomposite CeO/SrO can convert mechanical energy directly into chemical energy, thereby enabling mechanically oxidative sulfur desulfurization. 320 W of bath sonication were used to polarize and activate the prepared piezo-catalyst nanocomposite CeO/SrO for sulfur removal from thiophene and dibenzothiophene as model fuels and kerosene as a real fuel. Using uniform and spherical CeO/SrO nanocomposites resulted in the highest desulfurization rates of 95.4 %, 97.3 %, and 59.7 %, respectively, for thiophene and dibenzothiophene. This study examined the effect of several parameters, such as sulfur concentration, pH of fuel, dosage of CexOy/SrO nanocomposite, power and time of ultrasonic, and shaking time, on the piezo-desulfurization of thiophene (TP) and dibenzothiophene (DBTP). To identify the major active species in piezo desulfurization, radical trapping experiments were conducted. This study investigated the possibility of reusing the catalyst, and the piezo-desulfurization activity that was demonstrated in the removal of TP and DBTP after 11 cycles as well as the ability of the catalyst to remove real fuel even after 14 cycles was promising. As the kinetic results show, the reaction follows the second order with K = 0.0050. Also, thermodynamic results showed the oxidation of sulfide to sulfoxide and sulfoxide is endothermic. Activation energy for second order rate constant is (3.824 Kj/mole). 0.0236 mol. Sec was calculated for Arrhenius Constant.