Novel and eco-friendly solutions are extensively needed for wastewater treatment. This work capitalizes on the combination of waste vitrification and additive manufacturing to produce an efficient photocatalyst for the specific purpose. Fine powders of waste-derived glass, containing Fe3O4 inclusions, by simple suspension (for a solid loading of 65 wt %) in alkaline solution (5 M NaOH), were transformed into pastes for direct ink writing. 3D-printed reticulated scaffolds were stabilized by the progressive hardening of a zeolite-like gel, formed by glass/solution interaction, at nearly room temperature. The printed scaffolds were successfully tested for the removal of methylene blue, realized by combining the high sorption capacity of the gel with the catalytic activity of magnetite inclusions, under UV light. A complete degradation of methylene blue is achieved by 90 min exposure, comparing favorably with other reported photocatalytic materials, requiring from 60 to 360 min. The photocatalytic activity was tested for several cycles, with no significant degradation. In other words, a waste-derived material can be reused for multiple times, to remediate wastewaters, with evident benefits on waste minimization.

Download full-text PDF

Source
http://www.ncbi.nlm.nih.gov/pmc/articles/PMC10828805PMC
http://dx.doi.org/10.1016/j.heliyon.2024.e24737DOI Listing

Publication Analysis

Top Keywords

direct ink
8
ink writing
8
methylene blue
8
upcycling waste
4
waste derived
4
derived glass
4
glass high-performance
4
high-performance photocatalytic
4
photocatalytic scaffolds
4
scaffolds alkali
4

Similar Publications

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!