The impact of environmentally friendly supramolecular coordination polymers as carbon steel corrosion inhibitors in HCl solution: synthesis and characterization.

Two 3D-supramolecular coordination polymers (SCP1 & SCP2) have been synthesized and characterized by physicochemical and spectroscopic methods. In a solution of 1.0 M HCl, SCPs were used to prevent corrosion of carbon steel (CS). The inhibition productivity (%η) rises as the synthetic inhibitor dose rises, and the opposite is true as the temperature rises. The study was carried out using chemical (mass loss, ML) and electrochemical ( potentiodynamic polarization, PDP and electrochemical impedance microscopy, EIS) techniques, which showed %η reached to 93.1% and 92.5% for SCP1 & SCP2, respectively at 21 × 10 M, 25 °C. For the polarization results, SCPs behave as mixed-type inhibitors. With increasing doses of SCPs, the charge transfer resistance grew and the double layer's capacitance lowered. The creation of a monolayer on the surface of CS was demonstrated by the finding that the adsorption of SCPs on its surface followed the Henry adsorption isotherm. The parameters of thermodynamics were computed and explained. The physical adsorption of SCPs on the surface of CS is shown by the lowering values of free energy (∆G < - 20 kJ mol) and increasing the activation energy (E) values in presence of SCP1 & SCP2 than in their absence. Atomic force microscope (AFM) and scanning electron microscopy (SEM) demonstrated the development of a protective thin film of SCPs precipitated on the surface of CS. There is a strong matching between results obtained from experimental and theoretical studies. Results from each approach that was used were consistent.