TEM Investigation on the Dislocation Loops in Zirconium Alloy by Neutron and Kr+ Ion Irradiation Tests.

Neutron irradiation (E ≥ 1 MeV) and 400 keV Kr+ ion irradiation tests were carried out and compared to study the formation and growth mechanism of dislocation loops in zirconium alloys. The results show that, as the irradiation reached 1.9 × 1025 n/m2 and 1.0 × 1020 Kr+/m2, a large number of -type dislocation loops and a small amount of large-sized -type dislocations hundreds of nanometers or even micrometers in size are observed in both samples. EDS results confirmed that the concentrations of Nb and Fe in the -type dislocation loops are higher than that in the matrix. With the increases of the dislocation loop size, part of the loop structure will decompose into the twisted, small-sized dislocation lines. Between two of the small-sized dislocation lines, a cubic structure was observed.