Shear bond strength between standard or modified zirconia surfaces and two resin cements incorporating or not 10-MDP in their matrix.

Objective: This study aimed first to compare the shear bond strength between zirconia samples luted to enamel with a 10-MDP- containing resin cement (Panavia F2.0, Kuraray, Japan) and those luted with a resin cement using a separated 10-MDP monomer-containing bottle (Panavia V5, Kuraray, Japan). The second objective was to evaluate the bond stability after 150 days of aging in water, between enamel and zirconia ceramic surface enhanced with a glass-ceramic coating.

Materials And Methods: 80 specimens composed of ceramic cylinders and enamel disks were obtained, within eight experimental groups (n = 10). 60 zirconia cylinders (Katana STML zirconia, Kuraray, Japan) were assigned to 3 groups according to their surface treatment: milled/sintered surface (ZRCT), tribochemical silica-coating (Cojet™ Sand, 3 M ESPE, Seefeld, Germany) (ZRTC), and glass-ceramic coating (IPS e.max Zirpress) (ZRZP). 20 cylinders of lithium disilicate had a milled surface (IPS e.max CAD, Ivoclar-Vivadent, Schaan, Liechtenstein) (ECAD). The cylinders of each group were further divided into two subgroups according to the resin cement used: Panavia F2.0 (-PF) and Panavia V5 (-PV). All specimens were stored in distilled water for 150 days before shear bond strength (SBS) tests. The fracture mode was analyzed, and data were statistically computed (two-way ANOVA, post hoc Tukey test, p < 0.05, SPSS, IBM, v26).

Results: The ECAD-PF group recorded the highest SBS values (31.75 ± 2.2), and the ZRCT-PF group recorded the lowest values (5.59 ± 1.1). The two-way ANOVA test showed that ceramic surface treatment had a statistically significant effect on SBS (F (3,72) = 38.95, p < 0.001) while the type of ARC did not (F (1,72) = 2.40, p = 0.126). Tukey's post hoc test revealed no statistical difference between the ZRZP and the ZRTC or ECAD groups.

Conclusion: Within the limitations of this study, the PV resin achieved similar shear bond strength results between tribocoated zirconia and enamel compared to the one for glass-ceramic and enamel. Furthermore, a long-term durable bond, similar to the glass-ceramic one, was achieved with the heat pressed ceramic coated specimens. Thus, this new surface treatment could be recommended for anterior cantilever bridges for its fracture resistance and bonding ability.