Characterization of CO Adsorbed to Clean and Partially Oxidized Cu(211) and Cu(111).

Copper-based catalysts gain activity through the presence of poorly coordinated Cu atoms and incomplete oxidation at the surface. The catalytic mechanisms can in principle be observed by controlled dosing of reactants to single-crystal substrates. However, the interconnected influences of surface defects, partial oxidation, and adsorbate coverage present a large matrix of conditions that have not been fully explored in the literature. We recently characterized oxygen and carbon monoxide coadsorption on Cu(111), a nominally defect-free surface, and now extend our study to the stepped surface Cu(211). Temperature-programmed desorption of CO adsorbed to bare metal surfaces confirms that two sites dominate desorption from a saturated layer: atop terrace atoms of local (111) character and atop step edge atoms with CO bound more strongly to the latter. At low coverage, discrete CO resonances in reflection adsorption infrared spectra can be assigned to these sites: 2077 cm for extended (111) terraces, 2093 cm for step sites, and additional kink-adsorbed molecules at 2110 cm. With increasing coverage, in contrast to Cu(111), the infrared spectral features on Cu(211) evolve and shift as a consequence of dipole-dipole coupling between differentially occupied types of sites. Auger electron spectroscopy shows that exposure to background O oxidizes the (211) surface at a rate nearly 1 order of magnitude greater than (111); we argue that the resulting surface is stoichiometric CuO, as previously found for Cu(111). This oxide binds CO less strongly than the bare metal and the underlying crystal cut continues to influence the adsorption sites available to CO. On oxidized (111) terraces, broad absorption peaks at 2115-2120 cm; on oxidized Cu(211), CO adsorbed to step sites appears as a resolved secondary peak at 2144 cm. This suite of spectroscopic signatures, obtained under carefully controlled conditions, will help to determine the origin and fate of adsorbed species in future studies of reaction mechanisms on copper.