Influence of biopolymer composition and crosslinking agent concentration on the micro- and nanomechanical properties of hydrogel-based filaments.

Hydrogel filaments were manufactured using wet spinning technique, incorporating variations in the concentrations of sodium alginate, gelatin, and calcium chloride (crosslinking agent). The combination of biopolymer concentrations was determined using design of experiments (DoE) approach. The resulting filaments were produced from the developed hydrogels. Tensile and vertical strength analyses of the filaments were conducted using an electromechanical extensor. Atomic force microscopy was employed to evaluate the roughness, viscoelasticity, retraction, and deflection of the hydrogels. By employing DoE, a total of seventeen different combinations of biopolymers and crosslinkers were generated to construct the hydrogels. The filaments exhibited variations in electromechanical traction (measured in kPa) and produced distinct stress peaks. Furthermore, diverse roughness values were observed among the tested materials, with the combinations featuring higher concentrations of sodium alginate displaying the highest Young's modulus. This study demonstrates that manipulating the concentrations of biopolymers and crosslinking agents can modulate the micro and nanomechanical properties of biopolymeric filaments.