Influence of bio-coupling agent on interfacial interlocking compatibility and toughness of ultrafine bamboo charcoal/polylactic acid composite film.

Applications for polylactic acid (PLA) are significantly impacted by its poor mechanical properties and lack of thermal stability. The goal of this work is to bridge the gap of poor compatibility among the components and enhance their interface interlocking capability to improve the toughness and thermal stability. Ultrafine bamboo charcoal (UFBC) was treated through deep eutectic solvent (DES) method to deposit sodium lignosulfonate (LS) on its surface. LS was used with PLA as a bio-coupling agent to create an eco-friendly PLA composite film with a wide range of characteristics. Benefiting from the penetration of PLA to the internal pores in UFBC, the resultant L-UFBC/PLA film has a good mechanical interlocking structure. Ls can increase the compatibility and strengthen the interface interlocking capability through DES method, which greatly improves the mechanical properties of the system. In comparison to pure PLA one, the elongation at break was 136.24 % greater, and the crystallinity (Xc) increased from 1.09 % to 3.33 %. Furthermore, the thermal stability of the system was also improved, and the residual at 600 °C rose by 4.83 %. These characteristics offer the prepared L-UFBC/PLA film a wide range of potential applications in the packaging, medical, agricultural, and other sectors.