Characterizations and film-forming properties of different fractionated high-amylose maize starches subjected to hydroxypropylation.

Dual-modifications of jet milling and hydroxypropylation were used to improve the functional properties of maize starch (HM, containing 67 % amylose). The fractions obtained in three sizes (HM-S, HM-M, HM-L) were further treated with 10 % and 30 % propylene oxide (PO10 and PO30). The infrared peak of starch at 2794 cm indicated the successful introduction of hydroxypropyl groups. The molar degree of substitution (MS) increased with the degree of jet milling. The MS of HM-L-PO10 is 0.4, that of HM-M-PO10 is 0.7, and that of HM-S-PO10 is 0.9. The crystallinity of dual-modified HM increased, but the crystal type remained unchanged, still being B-type. Dual-modification significantly improved the performance of starch, and the higher the degree of modification, the better the optimization effect. The lowest enthalpy changes of gelatinization (ΔH = 3.49 J/g), the best freeze-thaw stability, the highest elongation at break (110.42 %) and transmittance (81.22 %) were shown in HM-S-PO30. The present study confirms that HM-S-PO30 films have the best physicochemical and mechanical properties, which provide new insights into optimizing starch-based packaging materials.