Background: Fracture resistance of post-core restoration depends on the design of the post, post diameter, post length, the type of adhesive cement used along with material of the core. Despite the different studies concerning the effect of post space diameter on the fracture resistance of endodontically treated teeth, more information regarding fracture resistance and the effect of different post space systems/materials and diameters is required.
Aim Of The Study: This study aimed to evaluate fracture resistance of endodontically treated teeth, restored with two post-core systems in different post space diameters.
Materials And Methods: Twenty freshly extracted maxillary central incisors were collected for this study. They were randomly divided into four groups according to intracanal post and its diameter. Group GN (glass-fiber post of 10-mm length and 1.3-mm diameter with composite core), group GW (glass-fiber post of 10-mm length and 1.75-mm diameter with composite core), group ZN (custom-made zirconia one-piece post-core of 10-mm length and 1.3-mm diameter) and group ZW(custom-made zirconia one-piece post-core of 10-mm length and 1.75-mm diameter). Fracture resistance for all samples was evaluated using the universal testing machine under a static load. The data was collected and statistically analyzed using One-Way ANOVA test. Modes of failure were assessed using stereomicroscope for each group.
Results: The highest mean fracture resistance was recorded in group GW (638.7 ± 285.1 N), followed by group ZW (598.5 ± 127.6 N), then GN group (442.8 ± 65.38 N). The lowest mean fracture resistance was recorded in group ZN (435.3 ± 117.3 N). One-Way ANOVA test revealed that there was no statistically significant difference in fracture resistance values among the groups.
Conclusion: Post space diameter had an impact over the fracture resistance of endodontically treated teeth. Modulus of elasticity of post material had a major effect on the fracture resistance and mode of failure along with the restorability of the restored tooth. However, there was no statistically significant difference among the tested groups.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC10714464 | PMC |
| http://dx.doi.org/10.1186/s12903-023-03730-4 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Gingival Soft Tissue Integrative Zirconia Abutments with High Fracture Toughness and Low-Temperature Degradation Resistance.
Biomater Res
January 2025
Hospital of Stomatology, Sun Yat-Sen University, Guangzhou 510055, China.
Low fracture toughness, low-temperature degradation (LTD) susceptibility, and inadequate soft tissue integration greatly limit the application of zirconia ceramic abutment. Integrating the "surface" of hard all-ceramic materials into the gingival soft tissue and simultaneously promoting the "inner" LTD resistance and fracture toughness is challenging. Composite ceramics are effective in improving the comprehensive properties of materials.
View Article and Find Full Text PDFFracture resistances of heat-treated nickel-titanium files used for minimally invasive instrumentation.
BMC Oral Health
January 2025
Department of Conservative Dentistry, School of Dentistry, Dental Research Institute, Dental and Life Science Institute, Pusan National University, Yangsan, Korea.
Background: This study compared the torsional resistance, bending stiffness, and cyclic fatigue resistances of different heat-treated NiTi files for minimally invasive instrumentation.
Methods: TruNatomy (TN) and EndoRoad (ER) file systems were compared with ProTaper Gold (PG). Torsional load, distortion angle, and bending stiffness were assessed using a custom device AEndoS, and toughness was calculated using the torsional data.
Early and multiple doses of zoledronate mitigates rebound bone loss following withdrawal of RANKL inhibition.
J Bone Miner Res
January 2025
Cancer Ecosystems Program, Garvan Institute of Medical Research, Sydney, NSW, Australia.
Rebound bone loss following denosumab discontinuation is an important barrier in the effective long-term treatment of skeletal disorders. This is driven by increased osteoclastic bone resorption following the offset of RANKL inhibition, and sequential osteoclast-directed therapy has been utilised to mitigate this. However, current sequential treatment strategies intervene following the offset of RANKL inhibition and this approach fails to consistently prevent bone loss.
View Article and Find Full Text PDFRobust Mechanically Interlocked Network Ionogels.
Angew Chem Int Ed Engl
January 2025
Shanghai Jiao Tong University, School of Chemistry and Chemical Engineering, 800 Dongchuan Road, 200240, Shanghai, CHINA.
Ionogels have attracted considerable attention as versatile materials due to their unique ionic conductivity and thermal stability. However, relatively weak mechanical performance of many existing ionogels has hindered their broader application. Herein, we develop robust, tough, and impact-resistant mechanically interlocked network ionogels (IGMINs) by incorporating ion liquids with mechanical bonds that can dissipate energy while maintain structural stability.
View Article and Find Full Text PDFImproved Black Phosphorus Nanocomposite Hydrogel for Bone Defect Repairing: Mechanisms for Advancing Osteogenesis.
Adv Healthc Mater
January 2025
Department of Implantology, School and Hospital of Stomatology, Cheeloo College of Medicine, Shandong University & Shandong Key Laboratory of Oral Tissue Regeneration & Shandong Engineering Research Center of Dental Materials and Oral Tissue Regeneration & Shandong Provincial Clinical Research Center for Oral Diseases, No.44-1 Wenhua Road West, Jinan, Shandong, 250012, China.
Bone defects caused by fractures and diseases often do not heal spontaneously. They require external agents for repair and regeneration. Bone tissue engineering is emerging as a promising alternative to traditional therapies like autografts and allografts.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!