Electrospun Cactus Mucilage/Poly(vinyl alcohol) Nanofibers as a Novel Wall Material for Dill Seed Essential Oil ( L.) Encapsulation: Release and Antibacterial Activities.

This study aimed to create long-lasting carriers by producing electrospun nanofibers loaded with dill seed ( L.) essential oil (DSEO), using cactus mucilage (CM) and poly(vinyl alcohol) (PVA). Continuous and uniform electrospun nanofibers with a diameter of 158 ± 18 to 230 ± 26 nm were successfully made from the CM/PVA blend solution and the CM/PVA/DSEO emulsion. Atomic force microscopy topographic images revealed that the electrospun nanofibers had a tubular morphology. The thermogravimetric curves of DSEO, CM, pure PVA, and electrospun nanofibers demonstrate that the polymers used and the essential oil have effective chemical interactions. The water contact angle results suggest that the manufactured nanofibers are hydrophilic. CM/PVA consistently achieves a remarkable encapsulation efficiency of 100% DSEO. The electrospun nanofibers enabled the controlled release of free and encapsulated DSEO, resulting in sustained long-term release. The agar disk diffusion technique was used to study the antimicrobial activity of electrospun nanofibers and nanofibers containing DSEO against Gram-positive and Gram-negative bacteria. With a minimum inhibitory concentration of 2.5 mg/mL and a minimum bactericidal concentration of 5 mg/mL, electrospun nanofibers containing DSEO demonstrated bacteriostatic and bactericidal activities against foodborne pathogenic bacteria ( and ). The DSEO-loaded electrospun nanofibers derived from carbohydrates show promise as an active interior coating for use in biomedical and food packaging applications.