Vivid Colored Cooling Structure Managing Full Solar Spectrum via Near-Infrared Reflection and Photoluminescence.

Colored radiative cooling (CRC) offers an attractive alternative for surface and space cooling, while preserving the aesthetics of an object. However, there has been no study on the CRC using phosphors in regard to vivid coloration, sophisticated performance investigation, retention of properties, functionality, and structural flexibility all at once. Thus, to manage the entire solar spectrum, a colored cooling structure comprising a near-infrared (NIR)-reflective bottom layer and a top colored layer with a phosphor-embedded polymer matrix is proposed. The structure is paintable, vividly colored, hydrophobic, and ultraviolet (UV) and water resistant. In the daytime outdoor measurement, the structure with red, orange, and yellow colors exhibited lower temperature than a control group using commercial white paint by 4.7 °C, 7.2 °C, and 7.4 °C, respectively. After precise theoretical and experimental time-tracing temperature validation, the CRC performance enhancement from NIR reflection and photoluminescence effects was thoroughly analyzed, and a temperature reduction of up to 16.1 °C was achieved for the orange-colored structure. Furthermore, experiments of hydrophobicity infusion and exposure to UV and deionized water verified the durability of the colored cooling structure. In addition, flexible-film-type colored cooling structures were demonstrated using different bottom reflective layers, such as a silver thin film and porous aluminum oxide particle-embedded poly(vinylidene fluoride--hexafluoropropylene), suggesting the potential applicability of these colored cooling structures for vivid-colored, functional, and durable CRC.