Degradation of Mechanical Properties of Graphene Oxide Concrete under Sulfate Attack and Freeze-Thaw Cycle Environment.

In this paper, firstly, the effects of graphene oxide on the mechanical properties of concrete were investigated. Secondly, the degradation and mechanism of the mechanical properties of graphene oxide concrete (GOC) under sulfate attack and a freeze-thaw environment were investigated. In addition, the dynamic modulus of elasticity (MOE) and uniaxial compressive strength (UCS) of the GOC were measured under different environmental conditions. According to the test results, the incorporation of graphene oxide in appropriate admixtures could improve the mechanical properties of concrete in these two working environments. It is worth noting that this effect is most pronounced when 0.05 wt% graphene oxide is incorporated. In the sulfate attack environment, the MOE and UTS of the GOC specimen at 120 cycles decreased by 22.28% and 24.23%, respectively, compared with the normal concrete specimens. In the freeze-thaw environment, the MOE and UTS of the GOC specimen at 90 cycles decreased by 13.96% and 7.58%, respectively, compared with the normal concrete specimens. The scanning electron microscope (SEM) analysis showed that graphene oxide could adjust the aggregation state of cement hydration products and its own reaction with some cement hydration crystals to form strong covalent bonds, thereby improving and enhancing the microstructure density.