Puncture Resistance and UV aging of Nanoparticle-Loaded Waterborne Polyurethane-Coated Polyester Textiles.

The goal of this research was to investigate the effect of different types of nanoparticles on the UV weathering resistance of polyurethane (PU) treatment in polyester-based fabrics. In this regard, zinc oxide nanoparticles (ZnO), hydrophilic silica nanoparticles (SiO (200)), hydrophobic silica nanoparticles (SiO (R812)), and carbon nanotubes (CNT) were mixed into a waterborne polyurethane dispersion and impregnated into textile samples. The puncturing resistance of the developed specimens was examined before and after UV-accelerated aging. The changes in chemical structure and surface appearance in nanoparticle-containing systems and after UV treatments were documented using microscopic pictures and infrared spectroscopy (in attenuated total reflectance mode). Polyurethane impregnation significantly enhanced the puncturing strength of the neat fabric and reduced the textile's ability to be deformed. However, after UV aging, mechanical performance was reduced both in the neat and PU-impregnated specimens. After UV treatment, the average puncture strength of all nanoparticle-containing systems was always greater than that of aged fabrics impregnated with PU alone. In all cases, infrared spectroscopy revealed some slight differences in the absorbance intensity of characteristic peaks for polyurethane polymer in specimens before and after UV rays, which could be related to probable degradation effects.