Mesoporous graphitic carbon electrodes derived from boat-fruited shells of Sterculia Foetida for symmetric supercapacitors for energy storage applications.

In recent years, intensive research efforts have focused on translating biomass waste into value-added carbon materials broadcasted for their significant role in energy and environmental applications. For the first time, high-performance carbonaceous materials for energy storage applications were developed from the multi-void structure of the boat-fruited shells of Sterculia Foetida (SF). In that view, synthesized mesoporous graphitic activated carbon (g-AC) via the combination of carbonization at various elevating temperatures of 700, 800, and 900 °C, respectively, and alkali activation by KOH, with a high specific surface area of 1040.5 m g and a mesopore volume of 0.295 cm g. In a three-electrode configuration, the improved electrode (SF-K900) exhibited excellent electrochemical behavior, which was observed in an aqueous electrolyte (1 M HSO) with a high specific capacitance of 308.6 F/g at a current density of 1 A/g, owing to the interconnected mesopore structures and high surface area of SF-K900. The symmetric supercapacitor (SSC) delivered the specific capacitance of 138 F/g at 1 A/g with a high energy density (ED) of 13.4 Wh/kg at the power density (PD) of 24.12 kW/kg with remarkable cycle stability and supercapacitive retention of 93% over 5000 cycles. Based on the findings, it is possible to develop low-cost active electrode materials for high-rate performance SSC using mesoporous g-AC derived from SF boat-fruited shells.