Three-Dimensional Printing of Polycaprolactone/Nano-Hydroxyapatite Composite Scaffolds with a Pore Size of 300/500 µm is Histocompatible and Promotes Osteogenesis Using Rabbit Cortical Bone Marrow Stem Cells.

BACKGROUND Many patients have bone defects that exceed the healing size. This study aimed to construct polycaprolactone/nano-hydroxyapatite (PCL/nHA) composite scaffolds with different pore sizes and investigate the osteogenesis and histocompatibility of cortical bone mesenchymal stem cells (BMSCs-C) seeded on it after inoculation. MATERIAL AND METHODS After mixing PCL and nHA proportionally, three-dimensional (3D) printing was used to print scaffolds. Porosity, compressive strength, and elastic modulus of PCL/nHA scaffolds were tested. The proliferation of BMSCs-C cells was examined and osteogenesis, chondrogenesis, and adipogenesis were evaluated. BMSCs-C cells were inoculated into 3D printing scaffolds, and histocompatibility between BMSCs-C cells and scaffolds was observed by the cell count kit (CCK-8) assay and LIVE/DEAD staining. After inoculating BMSCs-C cells into scaffolds, alkaline phosphatase (ALP) activity and calcium content were measured. RESULTS There was no obvious difference in characteristics between the 3 PCL/nHA composite scaffolds. The porosity, compressive strength, and elastic modulus of the 300/500-μm scaffold were between those of the 300-μm and 500-μm scaffolds. With increasing pore size, the mechanical properties of the scaffold decrease. BMSCs-C cells demonstrated faster growth and better osteogenic, adipogenic, and chondrogenic differentiation; therefore, BMSCs-C cells were selected as seed cells. PCL/nHA composite scaffolds with different pore sizes had no obvious toxicity and demonstrated good biocompatibility. All scaffolds showed higher ALP activity and calcium content. CONCLUSIONS The 300/500 μm mixed pore size scaffold took into account the mechanical properties of the 300 μm scaffold and the cell culture area of the 500 μm scaffold, therefore, 300/500 μm scaffold is a better model for the construction of tissue engineering scaffolds.