RF Welding of Dielectric Lossless Foam Particles by the Application of a Dielectric Heatable Coating with High Recycling Potential.

Due to its chemical structure and the resulting dielectric properties, the processing of the commonly used particle foam material, expanded polypropylene (ePP), is limited. Processing within the radio-frequency welding process is therefore only possible with the use of processing aids. In this paper, a new approach for the use of a solid and dielectric heatable coating for the production of three-dimensional welded components out of ePP is presented. For this purpose, three different types of water-soluble polymer polyvinyl alcohol (PVA) were analyzed as potential coating materials. The thermal and dielectric properties of the coating were further adjusted by a modification with glycerol. The maximum amount of glycerol tested was 25% by volume. It influences both the temperature development in the radio-frequency (RF) welding process as well as the adhesive bond between the ePP foam particles. It is shown that the 120 °C approach in the RF welding process resulted in a cohesive bond between the coating layers. In this way, bonded plates can be produced. In mechanical tests with compression of 20%, the manufactured plates show sufficient load capacity. Furthermore, it can be shown that a separation of PVA and ePP by type, and thereby a separation of the foam particles, is possible with the use of hot water. This might open a new way for recycling of particle foams.