Background: One of the greatest benefits of contemporary restorative dentistry is the creation of fixed partial dentures. The retention and durability of the fixed partial dentures may be improved by using a variety of tooth preparation methods, surface treatments, and luting resins.
Aim: To measure the shear binding strength of resin cement to saliva-contaminated lithium disilicate (LDS) ceramic after being exposed to various cleaning treatments.
Methodology: Over 30 LDS samples were examined. In Group 1, a cleansing solution comprising 15% zirconium oxide (Ivoclean) was employed for a duration of 20 s. This was succeeded by a rinsing phase lasting 15 s utilizing deionized water, followed by a 15-s period for drying. Subsequently, a final stage of air drying was conducted over a span of 15 s. In contrast, Group 2 underwent a washing procedure of 20 s involving a cleansing solution containing 30% sodium silicate. This was then ensued by a rinsing interval of 15 s with deionized water, succeeded by an air-drying process spanning 15 s. After applying cleaning solutions to the surface and adhering the specimens to the composite blocks using resin cement Multilink Automix (Ivoclar Vivadent, Schaan, Liechtenstein), the shear bond strength was assessed.
Results: Using a 30% sodium silicate solution (Group 2), we were able to get the highest mean shear bond strength value after saliva-contaminated LDS. Group 1, 15% zirconium oxide (Ivoclean) had the weakest decontamination agents as measured by mean shear bond strengths. The shear bond strength values of the two groups were found to vary significantly between individuals using the independent sample -test. LDs ceramic cleaned with a 30% sodium silicate solution had a higher shear bond strength than ceramic cleaned with Ivoclean (p<0.05).
Conclusion: The application of a 30% sodium silicate solution rendered the highest shear bond strength for saliva-contaminated LDS ceramic. In comparison, ceramic cleaned with Ivoclean exhibited notably lower shear bond strength values. The outcome of this investigation highlights the potential of diverse cleaning agents in influencing the adhesive qualities of resin cement, thereby contributing to the enhancement of fixed partial denture durability and efficacy.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC10541234 | PMC |
| http://dx.doi.org/10.7759/cureus.44389 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Force Nanoscopy Demonstrates Stress-Activated Adhesion between Iron-Regulated Surface Determinant Protein B and Host Toll-like Receptor 4.
ACS Nano
January 2025
Louvain Institute of Biomolecular Science and Technology, UCLouvain, Croix du Sud, 4-5, bte L7.07.07, B-1348 Louvain-la-Neuve, Belgium.
The iron-regulated surface determinant protein B (IsdB) has recently been shown to bind to toll-like receptor 4 (TLR4), thereby inducing a strong inflammatory response in innate immune cells. Currently, two unsolved questions are (i) What is the molecular mechanism of the IsdB-TLR4 interaction? and (ii) Does it also play a role in nonimmune systems? Here, we use single-molecule experiments to demonstrate that IsdB binds TLR4 with both weak and extremely strong forces and that the mechanostability of the molecular complex is dramatically increased by physical stress, sustaining forces up to 2000 pN, at a loading rate of 10 pN/s. We also show that TLR4 binding by IsdB mediates time-dependent bacterial adhesion to endothelial cells, pointing to the role of this bond in cell invasion.
View Article and Find Full Text PDFOutcome of Er, Cr:YSGG laser and antioxidant pretreatments on bonding quality to caries-induced dentin.
BMC Oral Health
January 2025
Conservative Dentistry Department, Faculty of Oral and Dental Medicine, Future University, Cairo, Egypt.
Background: This study aimed to assess the influence of different pretreatment protocols and antioxidants application on the shear bond strength (SBS) of universal adhesive to sound (SoD) and caries-induced dentin (CID).
Methods: One hundred and twenty posterior teeth had their occlusal enamel removed, then the specimens were divided into two main groups according to dentin substrates; SoD and CID, three subgroups according to pretreatments protocols control (no pretreatment), NaOCl-treated, and Er, Cr:YSGG-treated and two divisions according to antioxidant application (with and without sodium ascorbate (SA) application). All-Bond Universal (ABU) universal adhesives was applied in self-etch (SE) mode then resin composite discs were built.
Repair bond strength of composite resin to CAD/CAM glass-ceramic: influence of cleaning methods, surface treatments, and aging.
J Dent
January 2025
DDS, MS, PhD, Department of Dentistry, Federal University of Rio Grande do Norte, Natal, Brazil. Electronic address:
Objective: To evaluate the influence of different cleaning methods, surface treatments, and aging on the repair bond strength to a CAD/CAM glass-ceramic.
Materials And Methods: Forty-eight lithium disilicate CAD/CAM ceramic blocks were fabricated, sintered, and embedded in acrylic resin. After contamination with human saliva, they were divided according to the factors "Cleaning method" (Control-water/air spray, Air-particle abrasion with AlO, Ivoclean cleaning paste), "Surface treatment" (5% Hydrofluoric acid-HF + Silane, Monobond Etch & Prime-MEP), and "Aging" (thermocycling, no thermocycling).
A Mutant Complement Factor H (W1183R) Enhances Proteolytic Cleavage of von Willebrand Factor by ADAMTS13 Under Shear.
J Thromb Haemost
January 2025
Department of Pathology and Laboratory Medicine; Institute of Reproductive Medicine and Developmental Sciences, The University of Kansas Medical Center, Kansas City, KS 66160. Electronic address:
Background: A loss-of-functional mutation (W1183R) in human complement factor H (CFH) is associated with complement-associated hemolytic uremic syndrome; mice carrying a similar mutation (W1206R) in CFH also develop thrombotic microangiopathy but its plasma von Willebrand factor (VWF) multimer sizes were dramatically reduced. The mechanism underlying such a dramatic change in plasma VWF multimer distribution in these mice is not fully understood.
Objective And Methods: To determine the VWF and CFH interaction and how CFH proteins affect VWF multimer distribution, we employed recombinant protein expression, purification, and various biochemical and biophysical tools.
Dynamic Mechanical Properties and Energy Absorption Capabilities of Polyureas Through Experiments and Molecular Dynamic Simulation.
Polymers (Basel)
January 2025
State Key Laboratory of Chemical Safety, Qingdao 266000, China.
Polyurea (PUR) has been widely used as a protective coating in recent years. In order to complete the understanding of the relationship between PUR microstructure and its energy absorption capabilities, the mechanical and dynamic performance of PURs containing various macrodiol structural units were compared using material characterization techniques and molecular dynamic simulation. The results showed that the PUR polycarbonate diols formed as energy absorbing materials showed high tensile strength, high toughness, and excellent loss factor distribution based on the comparison of stress-strain tensile curves, glass transition temperatures, phase images, and dynamic storage loss modulus.