A bioinspired synthetic fused protein adhesive from barnacle cement and spider dragline for potential biomedical materials.

Biomaterials with excellent biocompatibility, mechanical performance, and self-recovery properties are urgently needed for tissue regeneration. Inspired by barnacle cement and spider silk, we genetically designed and overexpressed a fused protein (cp19k-MaSp1) composed of Megabalanus rosa (cp19k) and Nephila clavata dragline silk protein (MaSp1) in Pichia pastoris. The recombinant cp19k-MaSp1 exhibited enhanced adhesion capability beyond those of the individual proteins in both aqueous and non-aqueous conditions. cp19k-MaSp1 protein fiber scaffolds prepared through electrospinning have adequate hydrophilicity compared to cp19k and MaSp1 protein fiber scaffolds, and offer improved overall porosity compared to MaSp1 protein fiber scaffolds. The cp19k-MaSp1 protein fiber scaffolds showed excellent proteolytically stable properties because of only 9.6 % depletion after incubation in a biodegradation solution for 56 d. The cp19k-MaSp1 protein fiber scaffolds present remarkably high extreme tensile strength (112.7 ± 11.6 MPa) and superior ductility (438.4 ± 43.9 %) compared with cp19k (34.4 ± 8.1 MPa, 115.4 ± 32.7 %) and MaSp1 protein fiber scaffolds (65.8 ± 9.3 MPa, 409.6 ± 23.1 %), also 68.4 % of tensile strength was recovered by incubation in K buffer after multiple stretches, which create a favorable cell adhesion, growth, and proliferation environment for human umbilical vein endothelial cells (HUVECs). The improved biocompatibility, extensive adhesion, mechanical strength, and self-recovery properties make the bioinspired synthetic cp19k-MaSp1 a potential candidate for biomedical tissue reconstruction.