Antimicrobial, function, and crystalline analysis on the cellulose fibre extracted from the banana tree trunks.

Bioactive substances such as phenolic compounds, antioxidants, and antibacterial agents are found in natural fibres. In this study, banana fibre was extracted from the trunks of banana plants. Antibacterial activity, FTIR, XRD, and SEM analysis were performed to characterize the banana cellulose fibre, and also raw and alkali-treated banana fibre composite was fabricated with an epoxy matrix. Results of the antibacterial analysis indicate that this banana cellulose fibre strongly impedes bacterial growth with elevated inhibitory zones. The primary peaks observed at 1170 cm and 1426 cm by FTIR analysis correspond to C-O stretching, O-H bending, aliphatic ether, secondary alcohol, and carboxylic acid. The morphological analysis reveals the fibre quality, and the EDX analysis confirms the elements present in the banana cellulose fibre. The XRD results demonstrated a more significant proportion (76.8%) of the amorphous region. This study indicates that banana cellulose fibre could be a promising source of antimicrobial compounds. In addition, the mechanical properties of alkali-treated banana fibre composite were preferable to raw fibre composite by an average of 3% for this banana fibre composite. As a result, this composite can be used to manufacture automobile interior components, as it can reduce the sanitizing periods of interior components during winter months.