Electromechanical Coupling in Collagen Measured under Increasing Relative Humidity.

The functional role of collagen piezoelectricity has been under debate since the discovery of piezoelectricity in bone in 1957. The possibility that piezoelectricity plays a role in bone remodeling has generated interest in the investigation of this effect in relevant physiological conditions; however, there are conflicting reports as to whether collagen is piezoelectric in a humid environment. In macroscale measurements, the piezoelectricity in hydrated tendon has been shown to be insignificant compared to dehydrated tendon, whereas, at the nanoscale, the piezoelectric effect has been observed in both dry and wet bone using piezoresponse force microscopy (PFM). In this work, the electromechanical properties of type I collagen from a rat tail tendon have been investigated at the nanoscale as a function of humidity using lateral PFM (LPFM) for the first time. The relative humidity (RH) was varied from 10% to 70%, allowing the piezoelectric behavior to be studied dry, humid, as well as in the hydrated range for collagen in physiological bone (12% moisture content, corresponding to 40-50% RH). The results show that collagen piezoresponse can be measured across the humidity range studied, suggesting that piezoelectricity remains a property of collagen at a biologically relevant humidity.