In this study, we investigated the influence of the gamma-irradiation dose and the addition of the cross-linking agent (triallyl isocyanurate (TAIC)) on the thermal, mechanical and tribological properties of plant-derived polyamide 1010 (PA1010). PA1010 and PA1010/TAIC were extruded using a twin screw extruder and injection molded. These specimens were then irradiated with gamma-ray in air with doses of 20 and 50 kGy. After gamma-irradiation, the specimens were heat-treated to remove the free radicals generated in the polymer. The combination of gamma-irradiation and the addition of TAIC significantly changed the crystal structures of PA1010. Glass transition temperature increased with the addition of TAIC and, in particular, with increasing gamma-irradiation dose. Moreover, PA1010/TAIC showed a rubbery plateau originating from cross-links by gamma-irradiation, which was observed in the temperature regions above the melting point in DMA measurements. Mechanical properties such as strength, modulus and hardness, and tribological properties such as frictional coefficient, specific wear rate and limiting (pressure × velocity ) value of PA1010 improved with change in the internal microstructure with the gamma-irradiation and addition of TAIC.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC10384988 | PMC |
| http://dx.doi.org/10.3390/polym15143111 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Polyoxometalate-ionic liquids (POM-ILs) - a new type of ionic liquid additive family for lubricants.
RSC Adv
January 2025
Norwegian Tribology Center, Department of Mechanical and Industrial Engineering, Norwegian University of Science and Technology (NTNU) Trondheim Norway
The focus on energy efficiency to move towards a more sustainable use of resources has intensified efforts to minimize friction and wear in mechanical systems, which account for 23% of the world's energy consumption. In this study, polyoxometalate ionic liquids (POM-ILs) are introduced as environmentally acceptable lubricant additives, for their potential friction-reducing and anti-wear (AW) properties. These compounds, characterized by their complex structures and tunable properties, have been investigated for their tribological performance across base fluids of varying polarities.
View Article and Find Full Text PDFTribomechanical Properties of Glazes for Ceramic Tiles: A Novel Protocol for Their Characterization.
Materials (Basel)
December 2024
Department of Civil, Chemical, Environmental and Materials Engineering (DICAM), University of Bologna, Via Terracini 28, 40131 Bologna, Italy.
The aim of the work is to design and validate a characterization protocol for glazes used in the ceramic tile industry to lead manufacturers and researchers towards the formulation of glazes with enhanced wear resistance properties. The focus of the protocol is addressed to determine surface parameters that strongly depend on glaze formulation and firing temperature. This protocol includes analytical (e.
View Article and Find Full Text PDFTribological Properties of Selected Ionic Liquids in Lubricated Friction Nodes.
Materials (Basel)
December 2024
Faculty of Civil Engineering, Mechanics and Petrochemistry, Warsaw University of Technology, 09-400 Płock, Poland.
This article compares the rheological and tribological properties of three ionic liquids: Tributyl(methyl)phosphonium dimethyl phosphate 97%-MFCD, 1-Butyl-3-methylimidazolium hexafluorophosphate 97%-BMIMPF6, and 1-Butyl-3-methylimidazolium tetrafluoroborate 98%-BMIMBF4. Their density and kinematic viscosity at 20 °C and 40 °C were investigated, and tribological tests were carried out at the same temperatures with ball-on-disc contact. The test materials were made of 100Cr6 steel.
View Article and Find Full Text PDFEnhanced Tribological and Mechanical Properties of Copper-Modified Basalt-Reinforced Epoxy Composites.
Polymers (Basel)
January 2025
Department of Manufacturing Engineering, Technical University from Cluj-Napoca, 400001 Cluj-Napoca, Romania.
The increasing demand for high-performance materials in industrial applications highlights the need for composites with enhanced mechanical and tribological properties. Basalt fiber-reinforced polymers (BFRP) are promising materials due to their superior strength-to-weight ratio and environmental benefits, yet their wear resistance and tensile performance often require further optimization. This study examines how adding copper (Cu) powder to epoxy resin influences the mechanical and tribological properties of BFRP composites.
View Article and Find Full Text PDFTribological Performance of Short Fibers Reinforced Thermoplastic Polyurethane Composite Materials Under Water-Lubricated Condition.
Polymers (Basel)
December 2024
School of Transportation and Logistics Engineering, Wuhan University of Technology, Wuhan 430063, China.
The water-lubricated bearing plays a crucial role in the ship propulsion system, significantly impacting vessel safety. However, under the harsh working conditions of low-speed and heavy-load, the lubrication state of water-lubricated bearings is usually poor, leading to serious friction and wear. To improve the tribological performance of composites and reduce friction, three short fibers (ultra-high-molecular-weight polyethylene fibers, basalt fibers, and bamboo fibers) with the same mass fraction (5%) were added into the melted thermoplastic polyurethane (TPU).
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!