Background: Bleaching is a highly common method used nowadays to treat tooth discolouration because it is a significant cosmetic issue, particularly with anterior teeth, however bleaching itself results in microleakage.
Objective: This study aims to evaluate the impact of in-office bleaching on class V restoration microleakage with type 1 and type 2 composite restorations.
Methods: Three hundred and twenty healthy, caries-free removed human anterior teeth were used in this in-vitro study. All extracted teeth had their buccal and lingual surfaces uniformly prepped for class V cavities. The 120 removed teeth were divided into two groups, with Group 1 receiving Tetric N-Ceram nanohybrid composite restorations and Group 2 receiving 3 M Filtek Z350 XT nanohybrid composite restorations. Groups 1 and 2 were further broken into four more subgroups of four each. The restorations were sealed with a G-Coat Plus resin. The p-value was kept at 0.005 for the data analysis using the Chi-square and Fisher exact tests.
Results: Allocating microleakage among 320 study models revealed that 141 (44.1%) study samples had no microleakage, whereas 20 (6.3%), 54 (16.9%), and 105 (32.8%) study samples had microleakage up to, between, and greater than two-thirds of cavity depth. With a statistically significant p-value of 0.001, no microleakage was discovered in 85 (53.1%) lingual surfaces with Tetric N-Ceram nanohybrid composite restoration and 56 (35%) buccal surfaces with 3M Filtek Z350 XT nanohybrid composite restoration. 19.1% of samples of N-Ceram that were sealed and not bleached had no microleakage, according to analysis of microleakage across several groups. With a p-value of 0.001, the distribution of microleakage among various clusters was statistically notable.
Conclusion: According to the findings of the study, hydrogen peroxide bleaching has an enhanced impact on micro escape during dye dispersion. Both with and without bleaching, resin coating can be utilised to minimise marginal microleakage.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.3233/THC-230213 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Effect of antacid gastric syrups on surface properties of dental restorative materials: an in vitro analysis of roughness and microhardness.
BMC Oral Health
January 2025
Faculty of Dentistry, Department of Restorative Dentistry, Inonu University, Malatya, Turkey.
Objectives: The aim of this in-vitro study was to evaluate the effects of antacid gastric syrups on the surface roughness and microhardness of restorative dental materials.
Materials And Methods: Three different composite resins, nanohybrid, microhybrid and giomer, and four antacid gastric syrups were used in the study. A total of 150 samples were obtained by preparing 50 (10 mm x 2 mm) disk-shaped samples of each composite type.
Evaluation of the Mechanical Properties of Different Dental Resin-Based Materials After Submersion in Acidic Beverages.
Dent J (Basel)
December 2024
Faculty of Dental Medicine, Grigore T. Popa University of Medicine and Pharmacy Iasi, Str. Universitatii No. 16, 700115 Iasi, Romania.
: The aim of this study was to evaluate the influence of acidic beverages on the mechanical properties of various dental resin-based materials. : A total number of 160 samples were prepared using four types of resin-based materials-Group A ( = 40): flowable composite, Group B ( = 40): heavy-flow composite, Group C ( = 40): resin-based sealant and Group D ( = 40): nano-hybrid composite. Then, the samples were distributed into four subgroups according to the submersion solution: ( = 10): artificial saliva, ( = 10): coffee, ( = 10): cola and ( = 10): red wine.
View Article and Find Full Text PDFThe role of aging and various surface preparation methods in the repair of nanohybrid composites.
BMC Oral Health
January 2025
Faculty of Dentistry, Department of Restorative Dentistry, Gazi University, Bişkek St. 1. St. Number: 8 Emek, Ankara, Turkey.
Background: Repairing composite resins is a less invasive alternative to complete restoration replacement. To achieve a successful bond between the existing and newly applied composite materials, various surface preparation methods, such as sandblasting and acid etching, have been explored. The aim of the study was to evaluate the effect of different surface treatments on the repair bond strength of a universal nanohybrid composite resin restorative material before and after thermal aging, by utilizing a micro-shear bond strength (µSBS) test.
View Article and Find Full Text PDFUnlocking Advanced Architectures of Single-Crystal Metal-Organic Frameworks.
Angew Chem Int Ed Engl
January 2025
Fudan University - Handan Campus: Fudan University, Department of Chemistry, 2205 Songhu Road, Laboratory of Advanced Materials, 200438, Shanghai, CHINA.
The synthesis of metal-organic frameworks (MOFs) with diverse geometries has captivated considerable interest due to their manifestation of novel and extraordinary properties. While much progress has been made in shaping regular polyhedral single-crystal MOFs, the creation of more complex, topologically intricate nanostructures remains a largely unexplored frontier. Here, we present a refined site-specific anisotropic assembly and etching co-mediation approach to fabricate a series of hierarchical MOF nanohybrids and single-crystal MOFs.
View Article and Find Full Text PDFSurface Roughness and Color Stability of Conventional and Bulk-Fill Resin Composite with S-PRG Fillers After Coffee Exposure: An in-vitro Study.
Clin Cosmet Investig Dent
January 2025
Department of Restorative Dentistry, Faculdade de Odontologia de Piracicaba, Universidade Estadual de Campinas, Piracicaba, SP, Brazil.
Objective: This study aimed to evaluate the in vitro effects of coffee exposure on the color and roughness of conventional and bulk-fill resin composites, with and without surface pre-reacted glass-ionomer (S-PRG) filler.
Methodology: Forty-eight cylindrical samples (Ø6 mm × 2 mm) were prepared and categorized as follows (n = 12 per group): conventional nano-hybrid (Tetric N-Ceram, Ivoclar); nano-hybrid with S-PRG filler (Beautifil II, Shofu); bulk-fill (Tetric N-Ceram Bulk Fill, Ivoclar); and bulk-fill with S-PRG filler (Beautifil Bulk Restorative, Shofu). The samples were assessed for surface roughness (Ra, μm), color coordinates (CIE Lb), and overall color change (ΔE, ΔE).