Evaluation of physical/mechanical properties of an experimental dental composite modified with a zirconium-based metal-organic framework (MOF) as an innovative dental filler.

Objectives: This study aimed to modify an experimental dental composite using a synthesized nano-structured methacrylated zirconium-based MOF to enhance physical/mechanical properties.

Methods: The previously known Uio-66-NH MOF was first synthesized and post-modified with Glycidyl Methacrylate (GMA). Fourier Transform Infrared (FTIR) Spectroscopy and CHNS analysis confirmed the post-modification reaction. The prepared filler was investigated by XRD, BET, SEM-EDS, and TEM. The experimental composite was prepared by mixing 60% wt. of resin matrix with 40% wt. of fillers, including silanized silica (SS) or Uio-66-NH-Me (UM). The experimental composites' depth of cure (DPC) was investigated in five groups (G1 =40% SS, G2 =30%SS+10%UM, G3 =20%SS+20%UM, G4 =10%SS+30%UM, G5 =40%UM). Then flexural strength(FS), Elastic Modulus(EM), solubility(S), water sorption(WS), degree of conversion(DC), polymerization shrinkage(PS), and polymerization stress(PSR) of the groups with DPC of more than 1 mm were investigated. Finally, the cytotoxicity of composites was studied.

Results: The groups with more than 20% wt. UM, filler (G4, G5) had lesser than 1 mm DPC. Therefore, we investigated three groups' physical and mechanical properties with lower than 20% UM filler (G1-G3). Within these groups, G3 has a higher FS, EM (P < 0.05), and lower WS and S (P < 0.05). DC dropped in G2 and G3 compared to G1 (p < 0.05), but there was no significant difference between G2 and G3 (P = 0.594).

Significance: This new filler is an innovative coupling-agent free filler and can be part of dental filler technology itself. It can also introduce a new group of dental fillers based on MOFs, but it still needs a complete investigation to be widely used.