Green nanocoating-based polysaccharides decorated with ZnONPs doped Egyptian kaolinite for antimicrobial coating paper.

Paper coating plays an important role in the paper properties, printability and application. The nanocoating is a multifunction layer that provides the paper with unique features. In this work, nanocoating formulas were prepared using a green method and component. The nanocoating formulas were based on biopolymers nanostarch NSt and nanochitosan NCh (NCS) decorated with Egyptian kaolinite Ka doped with zinc nanoparticles NCS@xka/ZnONPs (x represents different ratios) support for multifunctional uses. The nanocoating formulas were characterized using a physiochemical analysis as well as a topographical study. FTIR, XRD, SEM and TEM techniques were used. Additionally, the antimicrobial activity of the tested samples was assessed against six microorganisms including Gram-negative and Gram-positive bacteria. The prepared nanocoating formulas affirmed excellent antimicrobial activity as a broad-spectrum antimicrobial active agent with excellent activity against all representative microbial communities. The nanocoating with the highest ratio of Ka/ZnONPs (NCS@40 ka/ZnONPs) showed excellent antimicrobial activity with an inhibition percentage of more than 70% versus all microorganisms presented. The paper was coated with the prepared suspensions and characterized concerning optical, mechanical and physical properties. When Ka/ZnONPs were loaded into NCS in a variety of ratios, the characteristics of coated paper were enhanced compared to blank paper. The sample NCS@40 ka/ZnONPs increased tensile strength by 11%, reduced light scattering by 12%, and improved brightness and whiteness by 1%. Paper coated with NCh suspension had 35.32% less roughness and 188.6% less porosity. When coated with the sample NCS@10 ka/ZnONPs, the coated paper's porosity was reduced by 94% and its roughness was reduced by 10.85%. The greatest reduction in water absorptivity was attained by coating with the same sample, with a reduction percentage of 132%.