Synergistically enhanced sodium ion storage from encapsulating highly dispersed cobalt nanodots into N, P, S tri-doped hexapod carbon framework.

Development of multitudinous heteroatoms co-doped carbon nanomaterials with pleasurable electrochemical behavior for sodium ion batteries is still an enormous challenge. Herein, high dispersion cobalt nanodots encapsulating into N, P, S tri-doped hexapod carbon (H-Co@NPSC) have been victoriously synthesized via H-ZIF67@polymer template strategy with using poly (hexachlorocyclophos-phazene and 4,4'-sulfonyldiphenol) as both carbon source and N, P, S multiple heteroatom doping sources. The uniform distribution of cobalt nanodots and the Co-N bonds are conducive to form a high conductive network, which synergistically increase a lot adsorption sites and lessens the diffusion energy barrier, thereby improving the fast Na ions diffusion kinetics. Consequently, H-Co@NPSC delivers the reversible capacity of 311.1 mAh g at 1 A g after 450 cycles with 70% capacity storage rate, while obtains the capacity of 237.1 mAh g after 200 cycles at the elevated current densities of 5 A g as an excellent anode material for SIBs. These interesting results pave a generous avenue for the exploitation of promising carbon anode materials for Na storage.