Clear polyurethane coatings with excellent virucidal properties: Preparation, characterization and rapid inactivation of human coronaviruses 229E and SARS-CoV-2.

Commercial polyurethane (PU) coating formulations have been modified with 1-(hydroxymethyl)-5,5-dimethylhydantoin (HMD) both in bulk (0.5 and 1% w/w) and onto the coatings surface as an N-halamine precursor, to obtain clear coatings with high virucidal activity. Upon immersion in diluted chlorine bleaching, the hydantoin structure on the grafted PU membranes was transformed into N-halamine groups, with a high surface chlorine concentration (40-43μg/cm). Fourier transform infrared spectroscopy (FTIR) spectroscopy, thermogravimetric analysis (TGA), energy-dispersive X-ray (EDX), X-ray photoelectron spectroscopy (XPS) and iodometric titration were used to characterize the coatings and quantify the chlorine contents of the PU membranes after chlorination. Biological evaluation of their activity against (Gram-positive bacteria) and human coronaviruses HCoV-229E and SARS-CoV-2 was performed, and high inactivation of these pathogens was observed after short contact times. The inactivation of HCoV-229E was higher than 98% for all modified samples after just 30 minutes, whereas it was necessary 12 hours of contact time for complete inactivation of SARS-CoV-2. The coatings were fully rechargeable by immersion in diluted chlorine bleach (2% v/v) for at least 5 chlorination-dechlorination cycles. Moreover, the performance of the antivirus efficiency of the coatings is considered as long-lasting, because experiments of reinfection of the coatings with HCoV-229E coronavirus did not show any loss of the virucidal activity after three consecutive infection cycles without reactivation of the N-halamine groups.