Crystal Chemistry and Photoluminescent Aspects of Bright Orange Light Emitting Sm- Activated BaBiVO Nanomaterials for Advanced Illuminating Applications.

In the present system, Sm activated BaBiVO nanomaterial series radiating orange-red light was developed via an efficient approach of solution combustion method. The structural examinations using XRD analysis indicate that the sample is crystallized into the monoclinic phase with the P21/a (14) space group. The elemental composition and morphological conduct were studied via energy dispersive spectroscopy (EDS) and scanning electron microscopy (SEM) respectively. Also, the formation of nanoparticles was confirmed by transmission electron microscopy (TEM). Photoluminescent (PL) examinations reveal the orange-red emission from the developed nanocrystals via documenting the emission spectra, which reveals the peak at 606 nm due to the G → H transition. Further, the decay time, non-radiative rates, quantum efficiency, and band gap of the optimal sample were computed as 1.3263 ms, 219.5 s, 70.88%, and 3.41 eV respectively. Finally, the chromatic parameters including color - coordinates (0.5565, 0.4426), 1975 K color correlated temperature (CCT), and color purity (85.58%) reflected their excellent luminous performance. The above-mentioned outcomes endorsed the relevancy of the developed nanomaterials as a propitious agent in the engineering of advanced illuminating optoelectronic appliances.