Pressure- and Rate-Dependent Mechanoluminescence with Maximized Efficiency and Tunable Wavelength in ZnS: Mn, Eu.

Mechanoluminescence (ML) has received widespread attention because of potential application in stress sensors and imaging. However, pursuing highly efficient ML remains a challenge due to multifactorial limitations such as pressure and loading rate. Here, we systematically investigate pressure- and rate-dependent ML in Mn and Eu co-doped ZnS in a gigapascal pressure range by using a high-pressure dynamic diamond anvil cell and microsecond time-resolved fluorescent methods and demonstrate the giant tunability in both ML efficiency and wavelength. Compressed from ambient pressure to 11 GPa at different compression rates, ZnS: Mn, Eu exhibits a volcano shape in ML emission efficiency with an optimum at ∼3.5 GPa and ∼211.1 GPa/s, at least 1000-fold higher than that measured in the MPa range. The pressure-dependent ML is accompanied with a tunable yellow-to-red emission color change. A combination of high-pressure X-ray diffraction and photoluminescence measurements reveals that the pressure- and rate-dependent ML behavior derives from pressure-induced strengthening of the crystal piezoelectric field and enhanced interaction between the host lattice and doped ions with a significant change of the energy level of the Mn ion. Significantly, the highly efficient ML of ZnS: Mn, Eu at the GPa level is reproducible under a compression-decompression process and can be manipulated on a micron scale, implying great potential in mechanical-optical energy conversion and application in dynamic pressure imaging, stress sensors, and multicolor displays.