Heterogeneous photo-Fenton catalyst α-FeO@g-CN@NH-MIL-101(Fe) with dual Z-Scheme heterojunction for degradation of tetracycline.

A novel photo-Fenton catalyst α-FeO@g-CN@NH-MIL-101(Fe) (FGN) with dual Z-scheme heterojunction was successfully prepared by hydrothermal method to degrade tetracycline (TC). The preparation conditions were optimized by orthogonal test, and the successful synthesis was confirmed by characterization analyses. The prepared FGN showed better light absorption performance, higher photoelectrons-holes separation efficiency, lower photoelectrons transfer resistance, and higher specific surface area and pore capacity compared with α-FeO@g-CN and α-FeO. The effects of experimental conditions on the catalytic degradation of TC were investigated. The degradation rate of 10 mg/L TC could reach 98.33% within 2 h when the dosage of FGN was 200 mg/L, and the degradation rate could remain 92.27% after 5 times of reuse. Furthermore, the XRD spectra and XPS spectra of FGN before and after reuse were compared to explore the structural stability and catalytic active sites of FGN, respectively. According to the identification of oxidation intermediates, three degradation pathways of TC were proposed. Through HO consumption experiment, radical-scavenging experiments, EPR results, the mechanism of the dual Z-scheme heterojunction was proved. The improved performance of FGN was attributed to the dual Z-Scheme heterojunction effectively promoting the separation of photogenerated electrons from the holes and accelerating the electrons transfer, and the increase of the specific surface area.