Carbonaceous materials are widely investigated as anodes for potassium-ion batteries (PIBs). However, the inferior rate capability, low areal capacity, and limited working temperature caused by sluggish K-ions diffusion kinetics are still primary challenges for carbon-based anodes. Herein, a simple temperature-programmed co-pyrolysis strategy is proposed for the efficient synthesis of topologically defective soft carbon (TDSC) based on inexpensive pitch and melamine. The skeletons of TDSC are optimized with shortened graphite-like microcrystals, enlarged interlayer spacing, and abundant topological defects (e.g., pentagons, heptagons, and octagons), which endow TDSC with fast pseudocapacitive K-ion intercalation behavior. Meanwhile, micrometer-sized structure can reduce the electrolyte degradation over particle surface and avoid unnecessary voids, ensuring a high initial Coulombic efficiency as well as high energy density. These synergistic structural advantages contribute to excellent rate capability (116 mA h g at 20 C), impressive areal capacity (1.83 mA h cm with a mass loading of 8.32 mg cm ), long-term cycling stability (capacity retention of 91.8% after 1200 h cycling), and low working temperature (-10 °C) of TDSC anodes, demonstrating great potential for the practical application of PIBs.

Download full-text PDF

Source
http://dx.doi.org/10.1002/smll.202302537DOI Listing

Publication Analysis

Top Keywords

topologically defective
8
defective soft
8
soft carbon
8
potassium-ion batteries
8
rate capability
8
areal capacity
8
working temperature
8
pseudocapacitive potassium-ion
4
potassium-ion intercalation
4
intercalation enabled
4

Similar Publications

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!