Effect of incorporating silica-hydroxyapatite-silver hybrid nanoparticles into the resin-modified glass ionomer on the adhesive remnant index score and shear bond strength of orthodontic metal brackets: An in vitro study.

Objectives: This study aimed to assess the effect of addition of silica-hydroxyapatite-silver (Si-HA-Ag) hybrid nanoparticles to light-cure glass ionomer (GI) on shear bond strength (SBS) of metal brackets bonded with this adhesive and the adhesive remnant index (ARI) score.

Material And Methods: In this in vitro experimental study, 50 sound extracted premolars were assigned to 5 groups (n=10) for orthodontic metal bracket bonding with BracePaste® composite, Fuji ORTHO™ pure resin modified GI (RMGI), and RMGI reinforced with 2wt%, 5wt% and 10wt% Si-HA-Ag nanoparticles. The SBS of brackets was measured by a universal testing machine. Debonded specimens were inspected under a stereomicroscope at×10 magnification to determine the ARI score. Data were analyzed by one-way ANOVA, Scheffe test, Chi-square test, and Fisher's exact test (alpha=0.05).

Results: The maximum mean SBS was recorded in BracePaste® composite followed by 2% RMGI, 0% RMGI, 5% RMGI and 10% RMGI. Only the difference between the BracePaste® composite and 10% RMGI was significant in this regard (P=0.006). The groups were not significantly different regarding the ARI scores (P=0.665). All the SBS values were within the clinically acceptable range.

Conclusion: Addition of 2wt% and 5wt% Si-HA-Ag hybrid nanoparticles to RMGI as orthodontic adhesive caused no significant change in SBS of orthodontic metal brackets while addition of 10wt% hybrid nanoparticles significantly decreased the SBS. Nonetheless, all the SBS values were within the clinically acceptable range. Addition of hybrid nanoparticles had no significant effect on the ARI score.