Chitosan based sorafenib tosylate loaded magnetic nanoparticles: Formulation and in-vitro characterization.

Biocompatible magnetic nanoparticles are used for various biomedical applications. This study reported the development of nanoparticles with magnetic properties by embedding magnetite particles in the drug-loaded, crosslinked matrix of chitosan. Sorafenib tosylate-loaded magnetic nanoparticles were prepared by a modified ionic-gelation method. Particle size, zeta potential, polydispersity index, and entrapment efficiency of nanoparticles were in the range of 95.6 ± 3.4 nm to 440.9 ± 7.3 nm, 12.8 ± 0.8 mV to 27.3 ± 1.1 mV, 0.289 ± 0.011 to 0.571 ± 0.011, and 54.36 ± 1.26 % to 79.67 ± 1.40 %, respectively. The XRD spectrum of formulation CMP-5 confirmed the amorphous nature of the loaded drug in nanoparticles. TEM image confirmed the spherical shape of nanoparticles. Atomic force microscopic image of formulation CMP-5 indicated a mean surface roughness of 10.3597 nm. The magnetization saturation of formulation CMP-5 was 24.74 emu/g. Electron paramagnetic resonance spectroscopy revealed that formulation CMP-5's g-Lande's factor was 4.27, which was extremely near to the 4.30 (usual for Fe ions). Residual paramagnetic Fe ions may be responsible for paramagnetic origin. The data suggests superparamagnetic nature of particles. Formulations released 28.66 ± 1.22 % to 53.24 ± 1.95 % and 70.13 ± 1.72 % to 92.48 ± 1.32 % of the loaded drug after 24 h in pH 6.8 and pH 1.2, respectively. The IC value of formulation CMP-5 was 54.75 μg/mL in HepG2 (human hepatocellular carcinoma cell lines).