Metal-Organic Framework Crystal-Glass Composite Membranes with Preferential Permeation of Ethane.

Metal-organic framework (MOF) glass is an easy to process and self-supported amorphous material that is suitable for fabricating gas separation membranes. However, MOF glasses, such as ZIF-62 and ZIF-4 have low porosity, which makes it difficult to obtain membranes with high permeance. Here, a self-supported MOF crystal-glass composite (CGC) membrane was prepared by melt quenching a mixture of ZIF-62 as the membrane matrix and ZIF-8 as the filler. The conversion of ZIF-62 from crystal to glass and the simultaneous partial melting of ZIF-8 facilitated by the melt state of ZIF-62 make the CGC membrane monolithic, eliminating non-selective grain boundaries and improving selectivity. The thickness of CGC membrane can be adjusted to fabricate a membrane without the need of a support substrate. CGC membranes exhibit a C H permeance of 41 569 gas permeation units (GPU) and a C H /C H selectivity of 7.16. The CGC membrane has abundant pores from the glassy state of ZIF-62 and the crystalline ZIF-8, which enables high gas permeance. ZIF-8 has preferential adsorption for C H and promotes C H transport in the membrane, and thus the GCG membrane exhibits ultrahigh C H permeance and good C H /C H selectivity.