Incorporation of Zirconium Oxide Nanoparticles in Adhesive Resin for Bonding of Brackets to Enamel Conditioned with Er,Cr:YSGG, Photodynamic Therapy, and Phosphoric Acid.

To evaluate the effect of enamel conditioning methods, that is, total-etch and rinse (TER), Er,Cr:YSGG (ECYL), and photodynamic therapy (PDT) on the shear bond strength (SBS) of orthodontic metallic brackets bonded using Zirconium oxide experimental adhesive (ZOEA). Sixty human incisor buccal surfaces were cleaned and allocated into three groups based on the method of enamel surface treatment, that is, TER using 37% phosphoric acid gel, methylene blue photosensitizer activated by PDT and ECYL ( = 20 each). Each group was further divided into two subgroups ( = 10) based on the type of adhesive, that is, ZOEA and experimental adhesive (EA). Metallic brackets were seated using composite resin. Samples were placed in a universal testing machine for SBS and failure mode using the ARI index. One-way analysis of variance and post hoc Tukey were used for multiple comparisons. ARI was presented in percentages in different investigated groups. TER+ZOEA (17.16 ± 0.41 MPa) displayed the highest bond integrity. However, group PDT+EA (11.34 ± 0.25 MPa) demonstrated the lowest bond scores. The intergroup comparison revealed that the TER system displayed significantly higher SBS values than the PDT and ECYL groups ( < 0.05). The intragroup comparison revealed that enamel conditioned with TER and brackets bonded with ZOEA and EA displayed comparable bond integrity ( > 0.05). Enamel conditioned with TER bonded to a metallic bracket displayed better bond strength than PDT and ECYL. Zirconium oxide nanoparticles incorporated in adhesive have proved to be promising in improving the bond integrity of adhesive.