Highly efficient yellow emission and abnormal thermal quenching in Mn-doped RbCdCl.

In this paper, Mn-doped RbCdCl metal halide single crystals were prepared by a hydrothermal method. The RbCdCl:Mn metal halide exhibits yellow emission with photoluminescence quantum yields (PLQY) as high as 88%. Due to the thermally induced electron detrapping, RbCdCl:Mn also displays good anti-thermal quenching (ATQ) behavior with thermal quenching resistance (131% at 220 °C). The increase in the photoionization and the detrapping of the captured electrons from the shallow trap states were appropriately attributed to this exceptional phenomenon based on thermoluminescence (TL) analysis and density functional theory (DFT) calculations. The relationship between the fluorescence intensity ratio (FIR) of the material and temperature change was further explored using the temperature-dependent fluorescence spectrum. It was used as a temperature measuring probe based on absolute sensitivity () and relative sensitivity () with the change in temperature. The phosphor-converted white light emitting diodes (pc-WLEDs) were fabricated using a 460 nm blue chip with a yellow phosphor, which has a color rendering index (CRI = 83.5) and a low correlated color temperature (CCT = 3531 K). Because of this, finding new metal halides with ATQ behavior for high-power optoelectronic applications may be made possible by our findings.