Dental decay still presents a major health problem among children. Its treatment usually requires the use of stainless steel crowns. This study compares the wear behavior of 316 L stainless steel and polyetheretherketone (PEEK) composite under identical test conditions. The wear tests were conducted in a reciprocating ball-on-plate tribometer (Plint TE67/R) using alumina balls as a counterface and artificial saliva as a lubricant at 37 °C to faithfully mimic oral conditions. The coefficient of friction (COF) and specific wear rate () values were determined and SEM/EDS examinations were performed to identify the predominant wear mechanisms. Results showed that PEEK exhibited a significantly lower coefficient of friction (COF = 0.094 ± 0.004) and thus lower wear volume (Δ = 0.0078 ± 0.0125 mm) and higher wear resistance, with an average value of specific wear rate of = 9.07 × 10 mmNm when compared to stainless steel (COF = 0.32 ± 0.03, Δ = 0.0125 ± 0.0029 mm, = 1.45 × 10 mmNm). PEEK was revealed to be a potential material for use in pediatric crowns due to its high wear resistance while overcoming the disadvantages associated with steel at both an aesthetic and biological level.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC10053974 | PMC |
| http://dx.doi.org/10.3390/ma16062420 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Manufacturing of Liposomes Using a Stainless-Steel Microfluidic Device: An Investigation into Design of Experiments.
Langmuir
January 2025
Department of Polymer and Materials Chemistry, Faculty of Chemistry & Petroleum Sciences, Shahid Beheshti University, P.O. Box 1983969411 Tehran, Iran.
Liposomes are highly beneficial nanocarrier systems due to their biocompatibility, low toxicity, and exceptional inclusiveness, which lead to improved drug bioavailability. For biological applications, accurate control over these nanoparticles' mean size and size distribution is essential. Micromixers facilitate the continuous production of liposomes, enhancing the precision of size regulation and reproducibility.
View Article and Find Full Text PDFEvaluation by Scanning Electron Microscopy and Energy Dispersive X-Ray Spectroscopy of the Effects of Root Canal Instrumentation on the Radicular Dentine.
Microsc Res Tech
January 2025
Faculty of Dental Medicine, Grigore T. Popa University of Medicine and Pharmacy, Iasi, Romania.
One area of technological advancement has been the shift from stainless steel hand tools to nickel-titanium (Ni-Ti) rotary tools. This paper aims to perform an in vitro comparative study to evaluate the efficacy of five endodontic manual and rotary instruments such as Kerr files, Orodeka Plex V, ProTaper Flydent NiTi super files, and ProTaper Flydent NiTi super files in combination with an ultrasonic endodontic E3D Diamantata EMS scaler used for root canal shaping. The following aspects were highlighted: effective removal of smear layer (SL) from the dentinal tubules in the coronal 1/3, middle 1/3, and apical 1/3 of the root canal, appearance of cracks in the dentinal walls by SEM analysis, and highlighting of dentin mineral content and remnant debris by EDX analysis.
View Article and Find Full Text PDFGreen Manufacture of Hydrated Polymers Coatings with On-Demand Mechanics and Lubricity Based on Novel Biobased Polymerizable Deep Eutectic Solvents.
ACS Appl Mater Interfaces
January 2025
State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000, China.
The aging population necessitates a critical need for medical devices, where polymers-based surface lubrication coating is essential for optimal functionality. In fact, lubrication and mechanical requirements vary depending on the service environment of different medical devices. Until now, key mean is still blank for general preparation of hydrophilic polymers-based lubrication coatings with on-demand mechanics and lubricity.
View Article and Find Full Text PDFInfluence of sterilization and exposure to the Ringer's solution on physicochemical properties of nitrocarburized 316 LVM steel.
Acta Bioeng Biomech
September 2024
Faculty of Materials Science and Engineering, Warsaw University of Technology, Warsaw, Poland.
The aim of the study was to investigate the influence of the nitrocarburizing process carried out in low temperature plasma using the active screen at 440 °C on the structure and physicochemical properties of the 316LVM steel. In the paper, results of micro-structure and phase composition of the layers, roughness, and surface wettability, potentiodynamic pitting corrosion resistance, penetration of ions into the solution as well as biological tests were present. The studies were conducted for the samples of both mechanically polished and nitrocarburized surfaces, after sterilization, and exposure to the Ringer's solution.
View Article and Find Full Text PDFListening to the Formation of Polymorphs in a Ball Mill.
Anal Chem
January 2025
ICGM, Univ. Montpellier, CNRS, ENSCM, 34000 Montpellier, France.
In this contribution, we apply our newly developed ball-milling platform, which combines Raman spectroscopy and thermal (IR) imaging, as well as acoustic and high-speed optical video recordings, to the synthesis and transformation of citric acid-isonicotinamide (1:2) cocrystal polymorphs in transparent PMMA jars. Particularly, we demonstrate how Raman, temperature, acoustic, and video data are complementary and enable detection and connection of chemical and physical events happening during ball-milling in a time-resolved manner. Importantly, we show that the formation of the three cocrystal polymorphs can be detected through acoustic analyses solely.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!