Effect of Fiber Fraction on Ballistic Impact Behavior of 3D Woven Composites.

This paper studies the ballistic impact performance of 3D woven composites (3DWCs) with hexagonal binding patterns. Para-aramid/polyurethane (PU) 3DWCs with three kinds of fiber volume fraction (V) were prepared by compression resin transfer molding (CRTM). The effect of V on the ballistic impact behavior of the 3DWCs was analyzed by characterizing the ballistic limit velocity (V50), the specific energy absorption (SEA), the energy absorption per thickness (E), the damage morphology and the damage area. 1.1 g fragment-simulating projectiles (FSPs) were used in the V50 tests. Based on the results, when the V increases from 63.4% to 76.2%, the V50, the SEA and the E increase by 3.5%, 18.5% and 28.8%, respectively. There are significant differences in damage morphology and damage area between partial penetration (PP) cases and complete penetration (CP) cases. In the PP cases, the back-face resin damage areas of the sample III composites were significantly increased to 213.4% of the sample I counterparts. The findings provide valuable information for the design of ballistic protection 3DWCs.