Covalent Bonding Enhanced Polypropylene Based T-ZIF-8 Masterbatch with Superior Photocatalytic and Antibacterial Performances.

In order to solve the problem of poor compatibility between modified-ZIF-8 nanoparticles and mask matrix polypropylene (PP) and melt-blown materials, in this work, PP based modified-ZIF-8 antibacterial masterbatch was prepared employing surface modification and torque blending method. IR, SEM, XRD, XPS, DSC results confirm that the antibacterial masterbatch maintains the chemical and crystal structure of modified-ZIF-8 and the thermal stability of PP. Photocatalytic performance indicates that the antibacterial masterbatch basically maintains the photoresponse range of modified-ZIF-8, has narrower band gap and the superior photocatalytic performance than that of modified-ZIF-8. The photocatalytic antibacterial mechanism of ·O and as antibacterial active species is revealed according to the energy band structure and free radical capture experiment. The photocatalytic antibacterial activity of the antibacterial masterbatch against and under different dosage holds that the relationship between antibacterial rate and antibacterial agent concentration conforms to Beta distribution, demonstrating second-order kinetic behavior. The antibacterial properties reach the maximum when the loading of modified-ZIF-8 is 2% of the total weight of PP and melt-blown materials. and could be completely killed when the simulated sunlight is irradiated for 30 min. These results indicate that PP based modified-ZIF-8 antibacterial masterbatch has potential application in photocatalytic antibacterial masks.