Effects of layer thickness and build angle on the microbial adhesion of denture base polymers manufactured by digital light processing.

Purpose: To investigate the effects of printing-layer thickness and build angle on the surface characteristics and microbial adhesion of denture base polymers manufactured by digital light processing (DLP).

Methods: Specimens were additively manufactured using DLP. The specimens were printed with different printing-layer thicknesses (25, 50, and 100 μm) and build angles (0°, 45°, and 90°). Scanning electron microscopy was used to observe the surface topography, and the arithmetical mean heights (S) were measured. Moreover, the initial Candida albicans (C. albicans) adhesion to the specimens was evaluated using an adhesion test. Finally, two-way ANOVA and Tukey's multiple comparison tests were conducted.

Results: The results regarding the S values exhibited a statistically significant interaction (F (4, 45) = 90.77, P < 0.0001). The build angle has a significant impact on the surface topography. Furthermore, quantitative results revealed that the printing-layer thickness significantly affected C. albicans adhesion (F (2, 99) = 6.96, P = 0.0015).

Conclusions: The surface roughness was significantly affected by the printing-layer thickness and the build angle. Additionally, the surface topography was mainly determined by the build angle. Furthermore, the adhesion of C. albicans to the DLP-printed denture surfaces was significantly affected by the printing-layer thickness but not by the build angle. Consequently, it is critical to decrease the thickness of the printing layer to produce digital dentures with optimal material properties.