Designing a Coupling Agent with Aliphatic Polyether Chain and Exploring Its Effect on Silica/Natural Rubber Nanocomposites under the Action of Non-Rubber Contents.

In order to prepare engineering tires with lower rolling resistance and better wet slip resistance in a more environmentally friendly way. In this study, a series of low volatile organic compound (VOC) M-Si69 coupling agents (x = 1, 2, 3, 4, 5, 6, which means the number of ethoxy group in bis-(γ-triethoxysilylpropyl)-tetrasulfide (Si69) substituted by the aliphatic polyether chain) were applied to silica/NR nanocomposites to prepare tire tread with excellent performance. Firstly, M-Si69 was substantiated as the best choice of M-Si69 and Si69 to achieve comprehensive optima in the mechanical properties of silica/NR nanocomposites characterized by dynamic and static mechanical properties. Afterwards, the modification of silica with M-Si69 induced by Non-Rubber Contents (NRCs) in silica/NR nanocomposites was revealed by comparing the filler network, micromorphology, and mechanical properties of isoprene rubber (IR) and NR nanocomposites. Furthermore, compared with Si69, the M-Si69 coupling agent was found to conspicuously reduce the energy loss and improve the safety performance of engineering tires according to evaluations of the rolling resistance and dynamic thermomechanical properties of the silica/NR nanocomposites. Finally, the critical function of M-Si69 in reducing ethanol (a kind of volatile organic compound (VOC)) emissions from the reaction of coupling agent and silica was disclosed by gas chromatography-mass spectrometry.