Highly Multifunctional Performances of Boron Nitride Nanosheets/Polydimethylsiloxane Composite Foams.

Although this kind of hexagonal boron nitride (h-BN)-filled polydimethylsiloxane (PDMS) multifunctional composite foam has been greatly expected, its development is still relatively slow as a result of the limitation of synthetic challenge. In this work, a new foaming process of BNNSs-PDMS, alcohol, and water three-phase emulsion system is employed to synthesize a series of high-quality BNNSs/PDMS composite foams (BSFs) filled with highly functional and uniformly distributed BNNSs. As a result of well-bonded interfaces between the BNNSs and PDMS, enhanced multiple functions of BSFs appeared. The BSFs can show complete resilience at a compressive strain of 90% and only 3.99% irreversible deformation after 100,000 compressing-releasing hyperelastic cycles at a strain of 60%. On the basis of their outstanding shape-memory properties, the maximum voltage value of compression-driven piezo-triboelectric (CDPT) responses of the BSFs is up to ∼20 V. Depending on the remarkable super-elastic and CDPT performances, the BSFs can be used for sensitive sensing of temperature difference and electromechanical responses. Also, in the range of 12-40 GHz, the BSF materials display ultralow dielectric constants between 1.1 and 1.4 with proper dielectric loss tangent values of <0.3 and exhibit an enhanced and broadened sound adsorption capacity ranging from 500 to 6500 Hz. Although BSFs have high porosities of >65%, their thermal conductivities can still reach up to 0.407 ± 0.039 W m K. Moreover, the BSF materials display favorable thermal stability, obviously reduced coefficient of thermal expansion, and good flame retardancy. All of these properties render the BSFs as a new category of excellent multifunctional material.