Mussel inspired multifunctional bovine serum albumin (BSA) coatings loaded with Baicalein (BAI) to enhance osteogenesis and resist oxidative stress for potential application on implant.

Oxidative stress is associated with most traumatic or pathological bone defects, and seriously affects the effect of implantation. The construction of antioxidative and osteogenic coatings is of great significance to accelerate the bone regeneration of implants. In this study, baicalein (BAI), a nature flavonoid drug, was loaded in bovine serum albumin (BSA) by desolvent method to prepare BAI-BSA composite protein, and tannic acid (TA)/BAI-BSA coatings were further built via layer by layer self-assembly technology. BAI-BSA possesses good biocompatibility that showed no cytotoxicity to osteoblasts and erythrocytes, and helps to enhance the activity of alkaline phosphatase (ALP) and promote the formation of osteogenic mineralized calcium nodules. After assembled with TA, BAI-BSA coating significantly promoted cell adhesion and in vitro osteogenic mineralization of MC3T3-E1. Moreover, BAI drug loading improved the antioxidative function of BSA coatings effectively. The scavenging rates of (TA/BAI-BSA-10) for ABTS and DPPH free radicals were 69.6 ± 16.1 % and 53.4 ± 2.4 %, respectively. At cellular level, the TA/BAI-BSA coating effectively inhibited the impact of oxidative stress on the oxidative damage of osteoblasts. The drug-loaded protein coatings possess both great antioxidative and osteogenic functions, which have important potential in the field of bone repair.