Shear-bond strength of different Self-Etching adhesive systems to dentin with or without laser irradiation before photopolymerization (A comparative Study).

Unlabelled: This study aimed at comparing shear-bond strength (SBS) of different self-etching adhesive systems (Clearfil S Bond Plus, G-Premio BOND and IBond) to dentin without or with diode-laser irradiation before photo-polymerization and to determine the effect of storage and thermo-cycling on SBS of adhesive systems.

Methods: The buccal surface of 84 extracted maxillary premolars was grounded to create flat surface. The specimens were allocated into 3 groups (n = 28) depending upon the adhesive systems, then each group was divided into two sub-group (I, II) (n = 14). After the placement of respective adhesive systems on the flat surface, adhesive system in group I was photo-polymerized immediately, while in group II, the adhesive systems were exposed to diode-laser before photo-polymerization. Composite cylinder (4 mm in diameter and 2 mm height) was built on the flat surface of each specimen. Then group I and II were divided into two sub-groups (n = 7) according to the storage time and thermo-cycling (1 day without thermo-cycling or 72 days with thermo-cycling) then all the specimens were stored in distilled water. The SBS was measured at the end of storage period. ANOVA, Duncan's Multiple Range Test and independent -test " ≤ 0.05" were used for data analysis.

Results: G-premio BOND showed the highest mean value of SBS followed by Clearfil S Bond plus without significant difference between them, while IBond revealed the least mean value. Laser irradiation had positive effect on the bond-strength of all tested adhesive systems. The results also showed that the storage with thermo-cycling had negative effect on the bond-strength in groups without laser irradiation for all tested adhesive systems, while for groups with laser irradiation, the reduction in the bond-strength of all tested adhesive systems was not significant.

Conclusion: Diode-laser application prior to photo-polymerization of self-etch adhesive systems significantly increased the bond-strength to dentin and can increase the durability of composite adhesion.