An Injecting Molding Method for Forming the HFRP/PA6 Composite Parts.

Carbon/glass fiber-reinforced polymer hybrid composite (HFRP) has the advantages of a light weight and high strength. For the lightweight design of automobile parts, composite parts made of HFRP and polymer materials are increasingly in demand. The method of the injection molding is usually adopted to fabricate composite part with HFRP and polymer materials. The connecting strength between the two materials has an important influence on the service life of the composite part. In this paper, HFRP and polyamide-6 (PA6) were used to fabricate a composite part by the injection molding method. In order to improve the connecting strength between HFRP and PA6, a kind of micro-grooves was fabricated on the HFRP surface. The micro-grooves on the surface of the HFRP provided sufficient adhesion and infiltrating space of molten PA6 material into the mold. In addition, the glass fiber in HFRP can also be used as nucleating agent to facilitate the rapid crystallization of PA6. The micro-grooves on the surface of HFRP were embedded into PA6 like nails, which could improve the connecting strength at the interface effectively. The paper investigated the effects of mold temperature, injection pressure, holding pressure and holding time on the injection quality and connecting strength of composite parts in detail. With a mold temperature of 240 °C, an injection pressure of 8 MPa, a holding pressure of 8 MPa and a holding time of 3 s, the maximum tensile strength of 10.68 MPa was obtained for the composite part. At the effect of micro-grooves, the tensile strength of the composite part could be increased by 126.27%.