High-Iron Bauxite Residue (Red Mud) Valorization Using Hydrochemical Conversion of Goethite to Magnetite.

Bauxite residue (BR), also known as red mud, is a byproduct of the alumina production using the Bayer process. This material is not used to make iron or other iron-containing products worldwide, owing to its high content of sodium oxide and other impurities. In this study, we investigated the hydrochemical conversion of goethite (FeOOH) to magnetite (FeO) in high-iron BR from the Friguia alumina refinery (Guinea) by Fe ions in highly concentrated alkaline media. The simultaneous extraction of Al and Na made it possible to obtain a product containing more than 96% FeO. The results show that the magnetization of Al-goethite and Al-hematite accelerates the dissolution of the Al from the iron mineral solid matrix and from the desilication product (DSP). After ferrous sulfate (FeSO·7HO) was added directly at an FeO:FeO molar ratio of 1:1 at 120 °C for 150 min in solution with the 360 g L NaO concentration, the alumina extraction ratio reached 96.27% for the coarse bauxite residue size fraction (Sands) and 87.06% for fine BR obtained from red mud. The grade of iron (total iron in the form of iron elements) in the residue can be increased to 69.55% for sands and 58.31% for BR. The solid residues obtained after leaching were studied by XRD, XRF, TG-DTA, VSM, Mössbauer spectroscopy, and SEM to evaluate the conversion and leaching mechanisms, as well as the recovery ratio of Al from various minerals. The iron-rich residues can be used in the steel industry or as a pigment.