Foam insulation materials are widely used in the construction industry due to their low thermal conductivity attributable to their microstructures and their low-conductivity blowing agents and affordability. In this study, we evaluate how the thermal performance of foam insulation materials used for the exterior walls of buildings, viz., extruded polystyrene (XPS), polyisocyanurate (PIR), and phenolic foam (PF), age over the life cycle of a building. To compare the aging of thermal performance during the life cycle of a building, each material was tested at 70 and 110 °C and with slicing acceleration according to EN and ISO standards. The thermal conductivity of each foam insulation material was measured using a heat flow meter at an operating temperature of 23 °C and converted into thermal resistance values. Different foam insulation materials have different aging procedures according to material-specific EN standards, while ISO 11561 applies the same procedure to all material classifications. Upon comparing the aged values according to ISO and EN standards to the initial values, the analysis showed a change rate of 23 to 26% in PIR and 18 to 20% in PF. In XPS, a rate of change of 10 to 23.8% was calculated. Our results indicated that the slicing acceleration induced a thermal resistance reduction rate about three times faster than aging at 70 °C. However, the long-term changed thermal resistance values of the foam insulation material applied via the calculating procedure specified in the ISO and EN standards were similar.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC9695631 | PMC |
| http://dx.doi.org/10.3390/polym14224926 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Ultralight Carbon Tube Foam-Derived SiC Nanofibrous Aerogels with Arbitrary Shape, Excellent Rigidity, and Resilience for Thermal Insulation.
ACS Appl Mater Interfaces
January 2025
School of Mechanics and Aerospace Engineering, Dalian University of Technology, Dalian 116024, P. R. China.
Ceramic aerogels are promising high-temperature thermal insulation materials due to their outstanding thermal stability and oxidation resistance. However, restricted by nanoparticle-assembled network structures, conventional ceramic aerogels commonly suffer from inherent brittleness, volume shrinkage, and structural collapse at high temperatures. Here, to overcome such obstacles, 3D ultralight and highly porous carbon tube foams (CTFs) were designed and synthesized as the carbonaceous precursors, where melamine foams were used as the sacrificial templates to form the hollow and thin-wall network structures in the CTFs (density: ∼4.
View Article and Find Full Text PDFHierarchical Biogenic-Based Thermal Insulation Foam.
ACS Nano
January 2025
Department of Materials Science and Engineering, University of Maryland, College Park, Maryland 20742, United States.
Biogenic-based foam, renowned for its sustainable and eco-friendly properties, is emerging as a promising thermal insulating material with the potential to significantly enhance energy efficiency and sustainability in building applications. However, its relatively high thermal conductivity, large-pore configurations, and energy-intensive manufacturing processes hinder its widespread use. Here, we report on the scalable, one-pot synthesis of biogenic foams achieved by integrating recycled paper pulp and in situ nanoporous silica formation, resulting in a hierarchical structure comprising both micropores and nanopores.
View Article and Find Full Text PDFPreparation of anti-shrinkage branched poly (butylene succinate-co-butylene terephthalate)/cellulose nanocrystal foam with excellent degradability and thermal insulation.
Int J Biol Macromol
January 2025
State Key Laboratory of Chemical Engineering, Shanghai Key Laboratory of Multiphase Materials Chemical Engineering, School of Chemical Engineering, East China University of Science and Technology, Shanghai 200237, China. Electronic address:
Branched poly (butylene succinate-co-butylene terephthalate) (BPBST) was synthesized by in-situ polycondensation to enhance the foamability of poly (butylene succinate-co-butylene terephthalate) (PBST) and was blended with cellulose nanocrystals (CNC) to address foam shrinkage. The introduction of 2 wt% CNC increased the crystallization temperature of BPBST from 66.6 °C to 87.
View Article and Find Full Text PDFPolyurethane microplastics and associated tris(chloropropyl)phosphate additives both affect development in larval fathead minnow Pimephales promelas.
Environ Toxicol Chem
January 2025
Department of Ecology and Evolutionary Biology, University of Toronto, Toronto, ON, Canada.
Microplastics (< 5 mm) are a diverse class of contaminants ranging in morphology, polymer type, and chemical cocktail. Microplastic toxicity can be driven by one or a combination of these characteristics. Most studies, however, evaluate the physical effect of the most commercially available polymers.
View Article and Find Full Text PDFThe Complex Valorization of Black Alder Bark Biomass in Compositions of Rigid Polyurethane Foam.
Materials (Basel)
December 2024
Latvian State Institute of Wood Chemistry, Dzerbenes Street 27, LV-1006 Riga, Latvia.
The use of black alder (BA) bark biomass in rigid polyurethane (PUR) foam compositions was the main task of investigation. Extractive compounds isolated from the bark through hot water extraction were used as precursors for bio-polyol synthesis via acid-free liquefaction with the polyether polyol Lupranol 3300 and through oxypropylation with propylene carbonate. The OH functionality and composition of the polyols were analyzed via wet chemistry and FTIR spectroscopy.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!