Effects of Air Plasma Modification on Aramid Fiber Surface and Its Composite Interface and Mechanical Properties.

In order to improve the interface and mechanical properties of aramid fiber (AF)-reinforced epoxy resin (EP) composites (AF/EPs), the surface modification of AF was carried out with atmospheric pressure air plasma, and the effects of plasma treatment time and discharge power on the AF surface and the interface and mechanical properties of AF/EPs were investigated. The results show that, when plasma treatment time was 10 min and discharge power was 400 W, AF showed the best modification effect. Compared to the unmodified material, the total content of active groups on the surface of AF increased by 82.4%; the contact angle between AF and EP decreased by 20%; the interfacial energy and work of adhesion increased by 77.1% and 19.1%, respectively; the loss of AF monofilament tensile strength was controlled at only 8.6%; and the interlaminar shear strength and tensile strength of AF/EPs increased by 45.5% and 10.4%, respectively. The improvement in AF/EP interfacial and mechanical properties is due to the introduction of more active groups on the AF surface with suitable plasma processing parameters, which strengthens the chemical bonding between the AF and EP matrix. At the same time, plasma treatment effectively increases the surface roughness of AF, and the mechanical meshing effect between the AF and EP matrix is improved. The synergistic effect of chemical bonding and mechanical meshing improves the wettability and interfacial bonding strength between the AF and EP matrix, which enables the load to be transferred from the resin to the fiber more efficiently, thereby improving the mechanical properties of the AF/EP.