Immobilization of heavy metals in biochar by co-pyrolysis of sludge and CaSiO.

Sludge pyrolysis has become an important method of sludge recycling. Stabilizing heavy metals in sludge is key to sludge recycling. Currently, research on the co-pyrolysis of sludge and industrial waste is limited. This study aims to explore the impact and mechanism of the co-pyrolysis of sludge and CaSiO (the main component of slag) and to achieve the concept of "treating waste with waste". To this end, we added different proportions of CaSiO (0%, 3%, 6%, 9%, 12%, and 15%) for the co-pyrolysis with sludge, and varied the pyrolysis temperatures (300, 400, 500, 600, and 700 °C) and retention times (15, 30, 60, and 120 min) to study heavy-metal stabilization in sludge. Consequently, the optimum dosage of CaSiO required for the immobilization of different heavy metals was 9% (Cu, Zn, Pb, and Cr) and 15% (Ni). The contents of Cu, Zn, Pb, Cr, and Ni in the stable state (oxidized and residual states) were 92.73%, 79.23%, 99.55%, 92.43% and 90.33% respectively. At a pyrolysis temperature of 700 °C, the steady-state proportions of Cr, Pb, and Zn were 88.12%, 90.21%, and 77.21%, respectively. At a pyrolysis temperature of 400 °C, the stable-Cu and -Ni contents were 97.21% and 99.43%, respectively. The optimal dwelling time was 15 min. The results showed that the CaSiO addition weakened the O-H stretching vibration peak intensity, promoted the formation of aromatic and epoxy ring structures, and enhanced the heavy-metal immobilization. Furthermore, the CaSiO decomposition during co-pyrolysis produced SiO, CaO, and Ca(OH), which helped stabilize heavy metals.