Anisotropic Magnetoresistance Evaluation of Electrodeposited NiFe Thin Film on Silicon.

In this study, a simple growth of permalloy NiFe (Py) thin films on a semiconductive Si substrate using the electrochemical deposition method is presented. The electrodeposition was performed by applying a direct current of 2 mA/cm during different times of 120 and 150 s and thin films with different thicknesses of 56 and 70 nm were obtained, respectively. The effect of Py thickness on the magnetic properties of thin films was investigated. Field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectroscopy (EDS), atomic force microscopy (AFM), ferromagnetic resonance (FMR), anisotropic magnetoresistance (AMR), and magneto-optic Kerr effect (MOKE) analyses were performed to characterize the Py thin films. It was observed that the coercivity of the Py thin film increases by increasing the thickness of the layer. Microscopic images of the layers indicated granular growth of the Py thin films with different roughness values leading to different magnetic properties. The magnetic resonance of the Py thin films was measured to fully describe the magnetic properties of the layers. The magnetoresistance ratios of deposited Py thin films at times of 120 and 150 s were obtained as 0.226% and 0.235%, respectively. Additionally, the damping constant for the deposited sample for 120 s was estimated as 1.36 × 10, which is comparable to expensive sputtered layers' characteristics.